Microestrutural and Magnetic Properties Characterization of PrFeCoB-Based Alloys and Permanent HD Sintered Magnets

SILVA, M. R. M. ; FIM, R. G. T. ; SILVA, S. C. ; CASINI, J. C. S. ; TAKIISHI, H. ;

Artigo:

The magnets were produced by powder metallurgy route, using powders obtained by hydrogenation-decrepitation method (HD). The compositions of the alloys were: Pr20FeBalB5Cu2 (33% wt.) and Pr14FebalCo16B6Nb0,1(AlSiCuGaGd)x (where x = 0,3 e 0,5) (67% wt.). The characterization of the alloys and the magnets produced have been carried out using backscattered electron microscopy (BEM), energy-dispersive X ray spectroscopy (EDXS), X ray diffraction (XRD), X ray fluorescence (XRF) and magnetic properties have been measured using a permeameter. The results revealed that the Fe-rich phase is prejudicial to magnetic properties and the improvement of the properties is due to the elimination of the Fe-rich phase by heat treatment (1343K for 20 hours). Therefore, the magnets produced by heat treated alloys presented a maximum energy product 50% higher when compared with the magnets produced by as-cast alloys. The magnet produced by Pr14FebalCo16B6Nb0,1(AlSiCuGaGd)0,5 heat treated alloy presented the best values for remanence (Br = 1.03 T), maximum energy product ((BH)máx = 201.6 KJ.m^-3) and intrinsic coercivity (iHc = 716.2 KA.m^-3).

Artigo:

Os ímãs foram preparados via metalurgia do pó, a partir de pós obtidos pelo processo de Decrepitação por Hidrogênio (HD). As composições das ligas utilizadas foram: Pr20FeBalB5Cu2 (33% em peso) e Pr14FebalCo16B6Nb0,1(AlSiCuGaGd)x (onde x = 0,3 e 0,5) (67% em peso). As ligas utilizadas e os ímãs produzidos foram caracterizados por Fluorescência de Raios-X (FRX), Microscopia Eletrônica de Varredura (MEV), Espectroscopia de Energia Dispersiva (EDS), Difração de Raios-X (DRX), e as propriedades magnéticas foram obtidas por meio de Permeâmetro. Os resultados mostraram que o ferro livre contido nas ligas é prejudicial às propriedades magnéticas dos ímãs, e que a otimização dessas propriedades, é devido à eliminação desse constituinte mediante a um tratamento térmico (1343K por 20 horas). Assim, os ímãs produzidos com as ligas tratadas termicamente apresentaram produto de energia máxima superior a 50% em relação aos ímãs produzidos com a liga não tratada. O ímã, produzido com a liga Pr14FebalCo16B6Nb0,1(AlSiCuGaGd)0,5 tratada termicamente, apresentou os melhores valores de remanência (Br = 1.03 T), produto de energia máximo ((BH)máx = 201.6 KJ.m^-3) e coercividade intrínseca (iHc = 716.2 KA.m^-3).

Download (PDF)

Palavras-chave: PrFeCoB magnets; Hydrogen decreptation, Rare-earth permanent magnets,

Palavras-chave: ,

DOI: 10.5151/phypro-vii-efa-019

Referências bibliográficas
  • [1] GUTFLEISCH, O et al. Adv.Mater. v.23, p.821-842, 201
  • [2] KNOBEL, M. Revista Ciência Hoje, v.36, p.18-26, 2005.
  • [3] TROUT, S.R. In XVII RARE EARTH PERMANENT MAGNET WORKSHOP, p. 1-5, 2002.
  • [4] WESCHENFELDER.F et al. Tecnol. Metal. Mater. Miner., v. 9, p. 309-315, 2012.
  • [5] POUDYAL, N.; LIU, J P. Journal of Physics D: Applied Physics. V. 46, p. 23, 2013.
  • [6] TAKIISHI, H. Estudo da Microestrutura e Propriedades de Ligas Magnéticas e Ímãs Permanentes de Terras Raras-Metais De Transição-Boro Processados Com Hidrogênio, Tese (Doutorado em Tecnologia Nuclear), Programa de Pós-Graduação em Tecnologia Nuclear, Instituto de Pesquisas Energéticas e Nucleares, Universidade de São Paulo, São Paulo, 2001.
  • [7] HARRIS, I.R.; NOBLE, C.; BAYLE, T. J.Less-Common Metal, v. 131, p. L1-L4, 1985.
  • [8] TAKIISHI, H.; LIMA, L.F.C.P., FARIA, R.N. Powder Techhnology, v.127, p.223-225, 2002.
  • [9] FARIA, R.N.; TAKIISHI, H.; LIMA, L.F.C.P.; COSTA, I. Journal of Magnetism and Materials, v.237, p.261-266, 2001.
  • [10] OLIVEIRA, M.C.L.; TAKIISHI, H.; COSTA, I.; FARIA, R.N. Mater. Sci. Forum, v.170, p.530-531, 2006.
Como citar:

SILVA, M. R. M.; FIM, R. G. T.; SILVA, S. C.; CASINI, J. C. S.; TAKIISHI, H.; "Microestrutural and Magnetic Properties Characterization of PrFeCoB-Based Alloys and Permanent HD Sintered Magnets", p. 73-76 . In: Anais do VII Encontro Científico de Física Aplicada [=Blucher Physics Proceedings, v.3 n.1]. São Paulo: Blucher, 2016.
ISSN 2358-2359, DOI 10.5151/phypro-vii-efa-019

últimos 30 dias | último ano | desde a publicação


downloads


visualizações


indexações