Study of the mechanical and metallurgical properties of sintered steels for valve seat inserts application

GOMES, M. P. ; SANTOS, I. P. ; MUCSI, C. S. ; COLOSIO, M. A. ; ROSSI, J. L. ;

Artigo:

The aim of this work was to study the valve seat insert (VSI) produced with three different alloys (mainly modified from the original AISI M3/2, M2 and D2 high-speed steels) from the mechanical and metallurgical point of view. These alloys modifications were intended as an alternative to replace cobalt and lead used in the original alloy due to their high cost and toxicological effect respectively. Such alloys have been developed for internal combustion engines VSI manufacture. The VSI studied in this work was previously produced by the powder metallurgy (P/M) route. The VSI production was performed using a uniaxial hydraulic press and a belt conveyor furnace. The VSI was submitted to metallic infiltration during the sintering process using copper as filler. The studies were performed according to standardized apparent density (ASTM C 373-88), apparent hardness (ASTM E 92-82) and radial crush strength (MPIF Standard 35) tests. The VSI produced with M3/2 alloy proved to be more advantageous considering the highest values obtained in the apparent hardness and radial crush strength tests.

Artigo:

O objetivo deste trabalho foi estudar o inserto para assento de válvula (do inglês VSI - Valve Seat Insert) produzido com três ligas diferentes (modificadas principalmente das ligas originais de aço rápido AISI M3/2, M2 e D2) do ponto de vista mecânico e metalúrgico. As modificações destas ligas foram pretendidas como uma alternativa para substituir o cobalto e o chumbo usados na liga original, devido ao seu custo elevado e efeito toxicológico respectivamente. Tais ligas têm sido desenvolvidas para a manufatura de VSI utilizados em motores à combustão interna. O VSI estudado neste trabalho foi produzido pela rota da metalurgia do pó (M/P). Este processo foi realizado utilizando-se uma prensa hidráulica de compactação e um forno contínuo de esteira. Os VSI foram submetidos a infiltração metálica durante a etapa de sinterização utilizando cobre como infiltrante. Os estudos foram determinados de acordo com testes padronizados, sendo eles: densidade aparente (ASTM C 373-88), dureza aparente (ASTM E 92-82) e resistência à ruptura radial (MPIF padrão 35). Os VSI produzidos com a liga M3/2 provaram ser mais vantajosos considerando-se os valores obtidos nos ensaios de dureza aparente e resistência à ruptura radial.

Download (PDF)

Palavras-chave: powder metallurgy, characterization, valve seat insert, high-speed steel,

Palavras-chave: metalurgia do pó, caracterização, inserto de assento de válvula, aço rápido,

DOI: 10.5151/phypro-vii-efa-015

Referências bibliográficas
  • [1] ASM International Handbook Committee, Metals Handbook Vol. 7. Powder Metal Technologies and Applications. ASM International, 10th ed., 1999 (electronic version).
  • [2] CHANG, I.; ZHAO, Y. Advances in Powder Metallurgy: Properties, processing and applications Woodhead Publishing, UK, 2013.
  • [3] Grupo Setorial de Metalurgia do Pó. A metalurgia do Pó: alternativa econômica com menor impacto ambiental, Metallum Eventos Técnicos, 1a ed., 2009.
  • [4] SANTOS, I. P. Processamento e caracterização de aços sinterizados para uso em insertos de assentos de válvulas. 201 Dissertação (Mestrado) - Instituto de Pesquisas Energéticas e Nucleares, IPEN-CNEN/SP, São Paulo. Online at: Accessed on: December 22th 2015.
  • [5] ASTM American Society for Testing and Materials. Standard Test Method for: Water Absorption, Bulk Density, Apparent porosity and Apparent Specific Gravity of Fired Whiteware Products. ASTM C 373-88, 1999.
  • [6] ASTM American Society for Testing and Materials. Standard Test Method for: Vickers Hardness of Metallic Materials. ASTM E 92-82, 2003.
  • [7] MPIF Metal Powder Industries Federation. Method for Determination of Crush Radial Strength. MPIF Standard 35, 1965.
Como citar:

GOMES, M. P.; SANTOS, I. P.; MUCSI, C. S.; COLOSIO, M. A.; ROSSI, J. L.; "Study of the mechanical and metallurgical properties of sintered steels for valve seat inserts application", p. 59-61 . In: Anais do VII Encontro Científico de Física Aplicada [=Blucher Physics Proceedings, v.3 n.1]. São Paulo: Blucher, 2016.
ISSN 2358-2359, DOI 10.5151/phypro-vii-efa-015

últimos 30 dias | último ano | desde a publicação


downloads


visualizações


indexações