Influence of Plasma Nitriding Process in Wear Strength of the F53 Superduplex Stainless Steel

Pereira Neto, J. O. ; Silva, R. O. ; Silva, E. H. ; Moreto, J. A. ; Rossino, L. S. ; Manfrinato, M. D. ;

Full Article:

In an attempt to improve a surface of super-duplex stainless steel was carried out ion plasma nitriding. The super-duplex stainless steel was nitriding by plasma process during 2 hours at the 350 – 570oC. As can be seen, the thermochemical treatment influenced the microhardness superficial due to kind of nitride formed. The microwear resistance decreased at 400oC due to formation different nitrides in surface, causing an increase in hardness and wear volume resistance.

Full Article:

Download (PDF)

Palavras-chave: plasma nitriding, super-duplex stainless steel, microwear,

Palavras-chave:

DOI: 10.5151/matsci-mmfgm-051-f

Referências bibliográficas
  • [1] C. E. Pinedo, Tratamento Superficial para aplicações Tribológicas. Metalurgia Andamp; Materiais. (2004) 162-169.
  • [2] J. C. Vendramim, Seleção de Materiais para Nitretação. ISOFLAMA Industria e Comércio de Equipamentos LTDA.
  • [3] K. L. Rutherford and I. M. A Hutchings, Micro-abrasive wear test with particular application to coated systems. Surface and Coatings Technology. 79 (1996) p. 231-239.
  • [4] W. D. Callister JR. Ciência e Engenharia de Materiais, LTC Livros Técnicos e Científicos, Rio de Janeiro, 2008.
  • [5] T. Christiansen and M. A. J. Somers, On the crystallography structure of S-phase. Scripta Materialia, 50 (2004) p. 35-37.
  • [6] A. Leyland and A. Matthews, On the significance of H/E ratio in wear control: a nanocomposite coating approach to optimized tribological behaviour. Wear, 246 (2000) p. 1-11.
  • [7] A. P. Tschiptschin and C. E. Pinedo, Estrutura e propriedades do aço inoxidável austenítico AISI 316L Grau ASTM F138 nitretado sob plasma à baixa temperatura. Revista Escola de Minas, 63-1 (2010) p. 137-141.
  • [8] G. C. A. Baldin, Caracterização Frente a Corrosão dos Aços Inoxidaveis Super Duplex Endurecidos Superficialmente por Nitretação a Plasma. Trabalho de Graduação, Universidade Federal do Rio Grande do Sul, 2010.
  • [9] R. C. Cozza, Estudo do Comportamento do Coeficiente de Desgaste e dos Modos de Desgaste Abrasivo em Ensaios de Desgaste Micro-Abrasivo, Dissertação, Universidade de São Paulo, 2006.
  • [10] E.I. Dalibon, Tribological properties of SiNx Films on PH Stainless Steel With and Without nitriding a pre-treatment. 11ª International Congress on Metallurgy Andamp; Materials Sam/Conamet, Procedia Materials Science, 1 (2012) p. 313-320.
Como citar:

Pereira Neto, J. O.; Silva, R. O.; Silva, E. H.; Moreto, J. A.; Rossino, L. S.; Manfrinato, M. D.; "Influence of Plasma Nitriding Process in Wear Strength of the F53 Superduplex Stainless Steel", p. 34-37 . In: Proceedings of the 13th International Symposium on Multiscale, Multifunctional and Functionally Graded Materials [=Blucher Material Science Proceedings, v.1, n.1]. São Paulo: Blucher, 2014.
ISSN 2358-9337, DOI 10.5151/matsci-mmfgm-051-f

últimos 30 dias | último ano | desde a publicação


downloads


visualizações


indexações