Microwear Behavior Study of Carburization and Ion Plasma Nitriding of P20 Steel

Manfrinato, M. D. ; Cruz, N. C. ; Rossino, L. S. ; Lopes, H. S. M. ; Pereira Neto, J. O. ; Moreto, J. A. ;

Full Article:

The P20 steel, mainly used in plastic molds, was thermochemical treated by ion plasma nitriding, solid and gas carburization. In this work, the solid and gas carburization were carried out at 925ºC in four different times. The ion plasma nitriding was performed at 520ºC in three different times. It was observed that the thermochemical treatment increases the microwear resistance of the studied material. The gas carburizing treatment produced a bigger surface microhardness. Longer times of treatment increase effectiveness of thickness layer in all cases. The solid carburization produced larger thickness layer than gas carburization and ion nitriding.

Full Article:

Download (PDF)

Palavras-chave: Gas carburizing, solid carburizing, ion plasma nitriding, P20, microwear.,

Palavras-chave:

DOI: 10.5151/matsci-mmfgm-059-f

Referências bibliográficas
  • [1] L. Sors. Moldes e Matrizes, Hemus, São Paulo, 2002.
  • [2] A. L. V. Costa e Silva, P. R. Mei. Aços e ligas especiais, 3 ed., Blucher, São Paulo, 2010.
  • [3] ASM Metals Handbook. Properties and Selection Irons, Steels and High Performance Alloys, v. 1, 2005.
  • [4] V. Chiaverini. Aços e Ferros Fundidos, 4 ed., ABM, São Paulo, 1977.
  • [5] Favorit Special Steels. AISI P20. Available in: http://www.favorit.com.br/produtos/acos-ferramenta/aco-aisi-p20/. Access in 08/07/2014.
  • [6] K. L. Rutherford, I. M. Hutchings. A micro-abrasive wear test with particular application to coated systems. Surface and Coatings Technology, 79 (1996) p 231-239.
  • [7] M. Wolfart Jr. Nitretação a Plasma do Aço ABNT 316L em Baixas Temperaturas, Doutorado, Universidade Federal do Rio Grande do Sul, 2002.
  • [8] R. F. Reis, W. H. Schreiner, P. C. Borges. Nitretação do Aço Inoxidável AISI 316L a Altas Temperaturas: Influência na Camada Nitretada, Revista Brasleira de Aplicações de Vácuo, 25-3 (2006) p. 183-187.
  • [9] R. R. Caetano, A. R. Franco Jr., C. E. Pinedo. Características De Formação Da Austenita Expandida Na Nitretação Por Plasma Do Aço Inoxidável Austenítico AISI 316 Grau ASTM F138, In: CBECIMAT, Anais, 2002.
  • [10] M. D. Manfrinato. Influência da Nitretação a Plasma no Comportamento em Fadiga dos Aços Inoxidáveis Austeníticos AISI 304 e 316, Dissertação, Escola de Engenharia de São Carlos USP, 2006.
  • [11] C. E. Pinedo. Nitretação Por Plasma para Endurecimento Superficial de Aços Ferramenta, MM, (2004) p.122-133.
Como citar:

Manfrinato, M. D.; Cruz, N. C.; Rossino, L. S.; Lopes, H. S. M.; Pereira Neto, J. O.; Moreto, J. A.; "Microwear Behavior Study of Carburization and Ion Plasma Nitriding of P20 Steel", p. 38-41 . In: Proceedings of the 13th International Symposium on Multiscale, Multifunctional and Functionally Graded Materials [=Blucher Material Science Proceedings, v.1, n.1]. São Paulo: Blucher, 2014.
ISSN 2358-9337, DOI 10.5151/matsci-mmfgm-059-f

últimos 30 dias | último ano | desde a publicação


downloads


visualizações


indexações